Copper Components Manufacturer in India

Copper Component Density

Copper Component Density : 8.96 g/cm³

Cu Forged Component

Cu Forged Component Melting Point: 1085°C

Copper Machined components

Copper Machined Components Grades : C12200,C10200 ,C11000

Copper Components

Copper Components Types: Machined, Turned , Forged

Copper Components

Copper Components

Table of Content


Which 3 test reports American Buyers should ask before finalising the material from India?


Test Report
Material Composition Report
Mechanical Properties Test
Surface Quality and Finish Report

ISO Certified Cu Forged Component Supplier in Mumbai

Copper Components Specification

Copper Components Manufacturer in India offering high-quality products in various sizes and finishes to Nigeria, Thailand, Argentina, Indonesia, and Colombia.

Copper Forged components Composition


CU Turned Parts Composition

  • Cu 99.95% , O2 0.03%

Copper Machined components Grades


Copper Machined components Grades

  • C12200 ,C10200 ,C11000 ,C10100 ,C10300 ,C10800
Copper Turned components Temperature


Copper Turned components Temperature

  • 750°C to 950°C.

Copper Machined Parts Types


Copper Machined Parts Types

  • Machined
  • Turned
  • Forged
CU Turned Parts Uses


CU Turned Parts Uses

  • Switch gears
  • Electrical boards
  • Transformers
Copper Alloy Turned Components Manufacturing Method

Copper Alloy Turned Components Manufacturing Method

  • Mining, Refining
  • Smelting, Fabrication.

Exporter of Copper Alloy Machined Components in Various Sizes as Per ISO, ASTM and DIN Standards

Copper Forged components Types


C12200 Copper Machined Parts

C12200 Copper Machined Parts

C10200 Copper Turned Parts

C10200 Copper Turned Parts

C10100 Copper Forged Components

C10100 Copper Forged Components

C10300 Copper Machined Components

C10300 Copper Machined Components

C10800 Copper Turned Components

C10800 Copper Turned Components


Get C12200 Copper Turned Components in UNC, BA and UNF Threads for Mechanical Parts and Electrical Connections Application

Copper Components Supplier in India perfect for many applications in various industries.

Cu Machined Components Application


Copper Machined Components Application


Stockist of UNS C10200 Machined Parts in Anodizing, Powder Coating and Electroplating Finish at Low Cost

Copper Turned components Surface Finish

  • Natural
  • Nickel Plated
  • Gold Plated
  • Zinc-Nickel
  • Deep Bright
  • Anodized
  • Tin Plated
  • Chrome Plated
  • Silver Plated

Refer to the C11000 Copper Turned Parts HSN Code and Properties

CU Turned Parts HSN Code


Copper Component HSN Code
Tubes 7411
Sheets-Plates 7409
Strips 7409
Fittings 7412
Bars 7407

Copper Machined Parts Chemical Composition


Copper

80%

Copper Alloy Turned Components Mechanical Properties


Standard Copper No. Mechanical Properties
Tensile strength (Mpa) Grain Size (mm) Elongation(%) Temper
ASTM B88 C11000 O200 O0.025 – O50
  O200 O0.040 – O60
C12200 O250 – – H58
JIS H3300 C1100 245 ~ 325 – – OL
O205 – O40
O265 – – H
C1220 O255 – – H
O205 O0.040 O40 OL
O205 0.025 ~ 0.060 O40 O
245 ~ 325 – – 1/2H
EN 1057 – O250 – O30 or 20 R250
O220 – O40 R220
O290 – O3 R290
ASTM B75 C11000 O205 O0.040 – O50
  O205 O0.040 – O60
C12200 O310 – – H80
O250 – – H58

C12200 Copper Forged Components Physical Properties


Property MaxValue (S.I.) Min Value (S.I.) Units (S.I.) Min Value Max Value Units
Density 8.94 8.93 Mg/m3 557.482 558.106 lb/ft3
Energy Content 130 100 MJ/kg 10833.9 14084 kcal/lb
Atomic Volume (average) 0.0073 0.0071 m3/kmol 433.268 445.473 in3/kmol
Maximum Service Temperature 400 350 K 170.33 260.33 °F
Latent Heat of Fusion 210 200 kJ/kg 85.9841 90.2833 BTU/lb
Bulk Modulus 145 130 GPa 18.8549 21.0305 106 psi
Ductility 0.5 0.04 0.04 0.5 NULL
Elastic Limit 330 45 MPa 6.5267 47.8625 ksi
Loss Coefficient 0.002 3.5e-005 3.5e-005 0.002 NULL
Poisson’s Ratio 0.35 0.34 0.34 0.35 NULL
Tensile Strength 390 210 MPa 30.4579 56.5647 ksi
Shear Modulus 49 44 GPa 6.38166 7.10685 106 psi
Young’s Modulus 133 121 GPa 17.5496 19.29 106 psi
Compressive Strength 330 45 MPa 6.5267 47.8625 ksi
Endurance Limit 140 70 MPa 10.1526 20.3053 ksi
Hardness 1150 400 MPa 58.0151 166.793 ksi
Fracture Toughness 100 40 MPa.m1/2 36.4019 91.0047 ksi.in1/2
Modulus of Rupture 330 45 MPa 6.5267 47.8625 ksi
Glass Temperature K °F
Minimum Service Temperature 0 0 K -459.67 -459.67 °F
Melting Point 1355 1320 K 1916.33 1979.33 °F
Specific Heat 388 372 J/kg.K 0.287875 0.300257 BTU/lb.F

Thermal Properties of C10200 Copper Machined Components


Thermal Expansion 16.8 30.24 32.22 17.9 10-6/K 10-6/°F
Thermal Conductivity 147 275.189 692.652 370 W/m.K BTU.ft/h.ft2.F
Resistivity 1.82 1.82 4.9 4.9 10-8 ohm.m 10-8 ohm.m

C11000 Copper Turned Components Equivalent Material


BS EN ISO
U.K Europe  
C111 CW114C Cu-S
C103 CW008A Cu-OF
C101 CW004A Cu-ETP
CC102 CW106C CuCr1Zr
C101 CW011A Cu-Ag-2
C101 CW013A Cu-Ag-4
C109 CW118C Cu-TEP
C101 CW012A Cu-Ag-3

Alloy Others UNS BS BS EN
    North America U K U K/Europe
C1-09 2.-15-45 C1-45-00 C1-09 CW-11-8C
C1-01 NF A5-1-11-8-1 C1-10-00 C1-01 CW-00-4A
C1-03 NF A5-1-11-8-1 C1-02-00 C1-03 CW-00-8A
C1-06 BS-28-70-; BS-28-71-; BS-28-74 C1-22-00-; C1-22-10-; C1-23-00 C1-06 CW-02-4A
C1-07 C1-42-00 C1-07 BS-28-71-; BS-28-75
C1-10 BS-14-33-, BS-38-39 C1-01-00 C1-10 CW-00-9A

Copper

Brass

Copper Nickel

Other Products